PERTANIKA JOURNAL OF SCIENCE AND TECHNOLOGY

Duplex stainless steel (DSS) is an important material used for corrosion resistance in various harsh environment plants such as petrochemical, offshore subsea component, and other chemical industries. An approximately equal amount of austenite and ferrite (A/F) ratio grants good mechanical properties and rust protection on. The detrimental intermetallic phase frequently occurs due to an unbalanced A/F ratio caused by the welding’s thermal cycle. Backing gas is commonly applicable in the field combined Gas Tungsten Arc Welding (GTAW) process. However, the use of backing gas to complete a single weld from root to cap joint required huge additional costs for consumables. Maintaining the thermal cycle in the welding parameter and GTAW process with ER2209 filler metal for DSS below 10 mm thick can reduce the backing gas sequence. The research aims to efficiently substitute full backing gas consumption, which meets a desirable quality in terms of corrosion resistance. The effect of backing gas reduction was studied. All specimens were tested by visua Vickers microhardness, metallography, ferrite content measurement, and electrochemical corrosion test. The visual test shows no defects beyond the range of the ASME IX acceptance and criteria. The evaluation comes from the ferrite scope and electrochemical corrosion test. The backing gas on the root weld shows a balance A/F ratio of around 38% ferrite content accepted in various standards. The backing gas sequence on the root until filler-pass obtained 0.04 mm/year, which is the desirable corrosion resistance and met the requirement of ASTM A932.

• ASTM A923-14. (2014). Standard test methods for detecting detrimental intermetallic phase in duplex austenitic/ferritic stainless steels. ASTM Internasional.

• ASTM G102-89(2015)e1. (2015). Standard practice for calculation of corrosion rates and related information from electrochemical measurements. ASTM Internasional.

• Badji, R., Bouabdallah, M., Bacroix, B., Kahloun, C., Belkessa, B., & Maza, H. (2008). Phase transformation and mechanical behavior in annealed 2205 duplex stainless steel welds. Materials Characterization, 59(4), 447-453. https://doi.org/10.1016/j.matchar.2007.03.004

• Baghdadchi, A., Hosseini, V. A., Hurtig, K., & Karlsson, L. (2020). Promoting austenite formation in laser welding of duplex stainless steel - Impact of shielding gas and laser reheating. Welding in the World, 65, 499-511. https://doi.org/10.1007/s40194-020-01026-7

• Betini, E. G., Gomes, M. P., Mucsi, C. S., Orlando, M. T. D. A., Luz, T. D. S., Avettand-Fènoël, M. N., & Rossi, J. L. J. M. R. (2019). Effect of nitrogen addition to shielding gas on cooling rates and in the microstructure of thin sheets of duplex stainless steel welded by pulsed gas tungsten arc welding process. Materials Research, 22(Suppl 1), Article e20190247. https://doi.org/10.1590/1980-5373-mr-2019-0247

• Bhattacharya, A., & Singh, P. M. (2007). Stress corrosion cracking of welded 2205 duplex stainless steel in sulfide-containing caustic solution. Journal of Failure Analysis and Prevention, 7(5), 371-377. https://doi.org/10.1007/s11668-007-9069-6

• Chan, K. W., & Tjong, S. C. J. M. (2014). Effect of secondary phase precipitation on the corrosion behavior of duplex stainless steels. Materials, 7(7), 5268-5304. https://doi.org/10.3390/ma7075268

• Charles, J. (2013). Corrosion resistance properties. In I. Alvarez-Armas & S. Degallaix-Moreuil (Eds.), Duplex Stainless Steels (pp. 47-114). John Wiley & Sons, Inc. https://doi.org/10.1002/9781118557990.ch2

• Chen, T. H., & Yang, J. R. (2002). Microstructural characterization of simulated heat affected zone in a nitrogen-containing 2205 duplex stainless steel. Materials Science and Engineering: A, 338(1-2), 166-181. https://doi.org/10.1016/S0921-5093(02)00065-5

• Chern, T. S., Tseng, K. H., & Tsai, H. L. (2011). Study of the characteristics of duplex stainless steel activated tungsten inert gas welds. Materials & Design, 32(1), 255-263. https://doi.org/10.1016/j.matdes.2010.05.056

• Conradi, M., Kocijan, A., Zorko, M., & Jerman, I. J. P. i. O. C. (2012). Effect of silica/PVC composite coatings on steel-substrate corrosion protection. Progress in Organic Coatings, 75(4), 392-397. https://doi.org/10.1016/j.porgcoat.2012.07.008

• Geng, S., Sun, J., Guo, L., & Wang, H. (2015). Evolution of microstructure and corrosion behavior in 2205 duplex stainless steel GTA-welding joint. Journal of Manufacturing Processes, 19, 32-37. https://doi.org/10.1016/j.jmapro.2015.03.009

• Giridharan, P. K., & Murugan, N. (2009). Optimization of pulsed GTA welding process parameters for the welding of AISI 304L stainless steel sheets. The International Journal of Advanced Manufacturing Technology, 40, 478-489. https://doi.org/10.1007/s00170-008-1373-0

• Gozarganji, E. H., Farnia, A., & Ebrahimnia, M. (2021). Effect of shielding gas composition on geometry and austenite formation in low power pulsed Nd: YAG laser welded 2205 duplex stainless steel. Archives of Metallurgy and Materials, 66, 187-195. https://doi.org/10.24425/amm.2021.134775

• Hertzman, S. (2001). The influence of nitrogen on microstructure and properties of highly alloyed stainless steel welds. ISIJ International, 41(6), 580-589. https://doi.org/10.2355/isijinternational.41.580

• ISO 15156-3. (2015). Petroleum and natural gas industries - Materials for use in H2S-containing environments in oil and gas production - Part 3: Cracking-resistant CRAs (corrosion resistant alloys) and other alloys. ISO.

• Karlsson, L., Pak, S., & Ryen, L. (1995). Precipitation of intermetallic phases in 22% Cr duplex stainless weld metals. Welding Journal, 74(1), 28-38.

• Kordatos, J., Fourlaris, G., & Papadimitriou, G. (2001). The effect of cooling rate on the mechanical and corrosion properties of SAF 2205 (UNS 31803) duplex stainless steel welds. Scripta Materialia, 44(3), 401-408. https://doi.org/10.1016/S1359-6462(00)00613-8

• Liou, H. Y., Hsieh, R. I., & Tsai, W. T. (2002). Microstructure and pitting corrosion in simulated heat-affected zones of duplex stainless steels. Materials Chemistry and Physics, 74(1), 33-42. https://doi.org/10.1016/S0254-0584(01)00409-6

• Lippold, J. C., Baeslack III, W. A., & Varol, I. (1988). Heat-affected zone liquation cracking in austenitic and duplex stainless steels. Welding Journal, 71(1), 1s-14s.

• Lippold, J. C., & Kotecki, D. J. (2005). Welding metallurgy and weldability of stainless steels. Wiley-VCH.

• Liu, Z., Fan, C. L., Ming, Z., Chen, C., Liu, A., Yang, C. L., Lin, S. B., & Wang, L. P. (2020). Gas metal arc welding of high nitrogen stainless steel with Ar–N2-O2 ternary shielding gas. Defence Technology, 17(3), 923-931. https://doi.org/10.1016/j.dt.2020.05.021

• Matsunaga, H., Sato, Y. S., Kokawa, H., & Kuwana, T. (2013). Effect of nitrogen on corrosion of duplex stainless steel weld metal. Science and Technology of Welding and Joining, 3(5), 225-232. https://doi.org/10.1179/stw.1998.3.5.225

• Muthupandi, V., Srinivasan, P. B., Shankar, V., Seshadri, S. K., & Sundaresan, S. (2005). Effect of nickel and nitrogen addition on the microstructure and mechanical properties of power beam processed duplex stainless steel (UNS 31803) weld metals. Materials Letters, 59(18), 2305-2309. https://doi.org/10.1016/j.matlet.2005.03.010

• Nana, S., & Cortie, M. B. (1993). Microstructure and corrosion resistance of experimental low-nickel duplex stainless steels. Journal of the Southern African Institute of Mining and Metallurgy, 93(11), 307-315.

• Ramirez, A. J., Lippold, J. C., & Brandi, S. D. (2003). The relationship between chromium nitride and secondary austenite precipitation in duplex stainless steels. Metallurgical and Materials Transactions A, 34(8), 1575-1597. https://doi.org/10.1007/s11661-003-0304-9

• Ramkumar, K. D., Mishra, D., Raj, B. G., Vignesh, M. K., Thiruvengatam, G., Sudharshan, S. P., Arivazhagan, N., Sivashanmugam, N., & Rabel, A. M. (2015). Effect of optimal weld parameters in the microstructure and mechanical properties of autogeneous gas tungsten arc weldments of super-duplex stainless steel UNS S32750. Materials & Design (1980-2015), 66, 356-365. https://doi.org/10.1016/j.matdes.2014.10.084

• Sales, A. M., Westin, E. M., & Colegrove, P. (2016). Effect of nitrogen in backing gas on duplex root weld properties of heavy-walled pipe. Welding in the World, 60(5), 877-882. https://doi.org/10.1007/s40194-016-0347-3

• Varbai, B., Adonyi, Y., Baumer, R., Pickle, T., Dobranszky, J., & Majlinger, K. (2019). Weldability of duplex stainless steels - Thermal cycle and nitrogen effects. Welding Journal, 98(3), 78-87. https://doi.org/10.29391/2019.98.006

• Varol, I., Lippold, J. C., & Baeslack, W. A. (1992). Welding of duplex stainless steels. In D. L. Olson & T. H. North (Eds.), Key Engineering Materials (Vol. 69, pp. 217-252). Trans Tech Publications Ltd. https://doi.org/10.4028/www.scientific.net/KEM.69-70.217

• Verma, J., & Taiwade, R. V. (2017). Effect of welding processes and conditions on the microstructure, mechanical properties and corrosion resistance of duplex stainless steel weldments - A review. Journal of Manufacturing Processes, 25, 134-152. https://doi.org/10.1016/j.jmapro.2016.11.003

• Wang, S., Ma, Q., & Li, Y. (2011). Characterization of microstructure, mechanical properties and corrosion resistance of dissimilar welded joint between 2205 duplex stainless steel and 16MnR. Materials & Design, 32(2), 831-837. https://doi.org/10.1016/j.matdes.2010.07.012

• Wu, M., Liu, F., Pu, J., Anderson, N. E., Li, L., & Liu, D. (2017). The microstructure and pitting resistance of weld joints of 2205 duplex stainless steel. Journal of Materials Engineering and Performance, 26(11), 5341-5347. https://doi.org/10.1007/s11665-017-2976-0

• Zhang, Z., Jing, H., Xu, L., Han, Y., & Zhao, L. (2016). Investigation on microstructure evolution and properties of duplex stainless steel joint multi-pass welded by using different methods. Materials & Design, 109, 670-685. https://doi.org/10.1016/j.matdes.2016.07.110